STUDI KONDUKTIVITAS ELEKTROLIT POLIMER KITOSAN/PVA+KOH

Conductiviy study of Chitosan/PVA+KOH polymer eletrolyte

Authors

  • R.Putri - Departemen Fisika, Universitas Muhammadiyah Riau
  • A.Maddu - Departemen Fisika, Institut Pertanian Bogor
  • Irzaman - Departemen Fisika, Institut Pertanian Bogor

DOI:

https://doi.org/10.37859/jp.v1i2.108
Keywords: polymer electrolyte, conductivity, chitosan

Abstract

The blend-based polymer electrolyte consisting of chitosan and polyvinyl alcohol (PVA) as host polymers and potassium hydroxide (KOH) as the complexing salt was studied. Polymer
electrolyte were obtained by the casting technique. An attempt was also made to investigate the effect of TiO2 concentration in the chitosan/PVA+KOH polymer electrolyte. The best ionic conductivity values of 1,105 x 10-2 S cm-1 at room temperature were obtained for the sample containing 35%wt of KOH and 1,210 x 10-2 S cm-1 for the sample containing 50% wt TiO2. The polymer electrolyte with good ionic conductivity properties were characterized by thermal analysis (DSC). The glass transition temperature about 75.30 °C for the optimum Chitosan/PVA+KOH

Downloads

Download data is not yet available.

Downloads

Published

2011-05-30

How to Cite

-, R., -, A., & -, I. (2011). STUDI KONDUKTIVITAS ELEKTROLIT POLIMER KITOSAN/PVA+KOH: Conductiviy study of Chitosan/PVA+KOH polymer eletrolyte. Photon: Jurnal Sain Dan Kesehatan, 1(2), 13–17. https://doi.org/10.37859/jp.v1i2.108

Issue

Vol. 1 No. 2 (2011): Jurnal Photon

Section

Physical Sciences

License

Each article is copyrighted © by its author(s) and is published under license from the author(s).

When a paper is accepted for publication, authors will be requested to agree with the Creative Commons Attribution-Noncommercial-No Derivative Works 4.0