Pengaruh Variasi Interlayer Terhadap Hasil Sambungan Material Dissimilar Menggunakan Mesin Las Gesek Rotary Tegak Bar Plate
DOI:
https://doi.org/10.37859/jst.v11i1.6665
Abstract
The aim of this research is to determine the effect of variations in interlayer thickness on welding time, interface area and hardness values in dissimilar material welded joints using a bar-plate upright rotary friction welding machine. The method used in this research: rotational speed 2,613 rpm, friction pressure 0.5 MPa, forging pressure 0.7 MPa, forging time 10 seconds and interlayer variations (without interlayer, 0.3 mm, 0.5 mm and 1 mm). Tests used in the research: liquid penetrant test, metallography, and Vickers. It can be analyzed that interlayer variations have an effect on welding time. The time results obtained from using an interlayer with a thickness of 0.3 mm resulted in a time of 142.1 seconds, a 0.5 mm interlayer of 168.7 seconds, and a 1 mm interlayer of 204.4 seconds. The results for specimens without using an interlayer obtained a time of 71.3 seconds. The thicker the interlayer used, the longer the welding time. In observing the interface area, giving interlayer variations of 0.3 mm, 0.5 mm and 1 mm had an effect on cracks and cavities where all specimens were not found to have cracks or cavities, but voids were found in welding without allowing interlayer variations. In testing the hardness of interlayer variations with a thickness of 1 mm, the highest hardness was found in the interface area with an average hardness value of 169.56 VHN. Meanwhile, the lowest hardness value in the interface area results from variations without an interlayer with an average hardness value of 149.07 VHN
Downloads
References
Utamar, F. dan Siswanto. 2014. Perancangan Dan Pembuatan Mesin Las Gesek Rotari Tegak Bar-Plate. 9. Universitas Riau.
Dawood, H.I., Mohammed, K.S. Rahmat, A. & Uday, M. B. (2015). Microstructural characterizations and mechanical properties in friction stir welding technique of dissimilar (Al-Cu) sheets. Journal of Applied Science and Agriculture. 10(5): 149-158.
Meshram, S.D. & Reddy, G.M. 2015. Friction welding of aa6061 to aisi 4340 using silver interlayer. Defence Technology. 11(3): 292-298.
Heriansyah, M. dan Yohanes. 2021. Interlayer Effect on Connection of Mild Steel ST37 and Stainless Steel 201 on Ro1tary Friction Welding. Journal of Ocean, Mechanical and Aerospace. 65 (1). 32-30.
Yohanes and Meipen, Effect of Rotational Speed on Hardness Value and Area of Vertical Bar-Plate Rotary Friction Weld Joint. Journal of Ocean. 66(3).
Article 6. Section V. 2010.
Manurung, V.T., Wibowo, Y.T.J., dan Baksoro, S,Y. 2020. Panduan Metallografi. Edisi 1. Jakarta.
Wicaksana, H., Mulyadi, S., dan Syuhri, A. 2016. Sifat Mekanik Dan Struktur Mikro Sambungan Las Aluminium 6061 Hasil Friction Welding. Jurnal ROTOR. 9(1).
Purnomo, A. 2018. Struktur Mikro Sambungan Friction Welding Antara Bahan Paduan Tembaga Dan Paduan Aluminium Akibat Waktu Tekananerbeda. Jurnal Rekayasa Mesin. 10(3).77-81.
M. Simorangkir, Yohanes and M. Badri. 2023. Effect of Spindle Speed of Bar-Plate Rotary Friction Welding Machine on Joint Interface Area and Hardness Value. Journal of Ocean. 67(1)34–39.
Fatha, F. 2019. Optimasi Sambungan Rotary Friction Welding (RFW) Pada Aluminium Dengan Variasi Bentuk Profil Sambungan. Skripsi. Universitas Islam Indonesia.
Anitha, P., Majumder, M.C., Saravanan, V., dan Rajakumar, S. 2018. Microstructural Characterization and Mechanical Properties of Friction Welded IN718 and SS410 Dissimilar Joint. Springer Science + Business Media, LLC, part of Springer Nature and ASM International 2018. 7(3).
Purnomo, S. 2016. Pengaruh Variasi Gesek Terhadap Kualitas Sambungan Pada Pengelasan Continous Drive Friction Welding (CDFW) Bahan Pipa Kuningan Dan Tembaga. Skripsi. Universitas Muhammadiyah Yogyakarta.
Ananthapadmanaban, D., V. S. Rao., N. Abraham. & K. P. Rao. 2009. A study of mechanical properties of friction welded mild steel to stainless steel joints. Materials and Design. 30(7): 2642-2646.
Jun, T. S., F. Ratundo., X. Song., L. Ceschini., dan A. M. Korsunsky. 2010. Residual strains in AA2024/AlSiCp composite linear friction welds. Materials and Design. 31(1): 117-120.